Polyethylene chlorinated ad magna Products
chlorinated polyethylene ad Magnetica Products
| Item | Unitas | Type | ||||
| CPE3615G | CM2500A | CM2500B | CPE230A | CPE230B | ||
| Chlorum Content | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
| Calor eget | J/g | ≤5.0 | ≤10.0 | ≤2.0 | ≤2.0 | ≤2.0 |
| Litore duritia | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
| Distrahentes fortitudo | Mpa | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 |
| Elongation at Break | % | ≥800 | ≥600 | ≥600 | ≥800 | ≥800 |
| Volatile Content | % | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 |
| Viscositas Mooney | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
| Nota: Quaeso nobis confirmari cum speciales exigentias habes. | ||||||
| Item | Unitas | Type | ||||
| CPE3615G | CM2500A | CM2500B | CPE230A | CPE230B | ||
| Chlorum Content | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
| Calor eget | J/g | ≤5.0 | ≤10.0 | ≤2.0 | ≤2.0 | ≤2.0 |
| Litore duritia | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
| Distrahentes fortitudo | Mpa | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 |
| Elongation at Break | % | ≥800 | ≥600 | ≥600 | ≥800 | ≥800 |
| Volatile Content | % | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 |
| Viscositas Mooney | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
| Nota: Quaeso nobis confirmari cum speciales exigentias habes. | ||||||